KOLFARVERKSTÁL U7A/U7, C70U, C70W1, C70W2, 1.1520, 1.1620 SAMKVÆMT PN-H-85020, DIN 17350, ISO 4957.
| staðall | Stálgráða | ||||||
|---|---|---|---|---|---|---|---|
| Efnasamsetning prósent | |||||||
| C: | mn: | Já: | Q: | S: | Cr: | Hvorugt: | Cu: |
| PN | N7E | ||||||
| 0.65 - 0.74 | 0.15 - 0.30 | 0.15 - 0.30 | <0.025 | <0.025 | <0.15 | <0.20 | <0.20 |
| PN | N7 | ||||||
| 0.65 - 0.74 | 0.15 - 0.35 | 0.15 - 0.35 | <0.030 | <0.030 | <0.20 | <0.25 | <0.25 |
| GOST | U7A - У7А | ||||||
| 0.65 - 0.74 | 0.17 - 0.28 | 0.17 - 0.33 | <0.025 | <0.018 | <0.20 | <0.25 | <0.25 |
| GOST | U7 - У7 | ||||||
| 0.66 - 0.73 | 0.20 - 0.40 | 0.15 - 0.35 | <0.030 | <0.028 | <0.20 | <0.25 | <0.25 |
| ISO | C70W1 - C70U - 1.1520 | ||||||
| 0.65 - 0.75 | 0.10 - 0.40 | 0.10 - 0.30 | <0.030 | <0.030 | - | - | - |
| DIN | C70W2 - 1.1620 | ||||||
| 0.65 - 0.74 | 0.10 - 0.35 | 0.10 - 0.30 | <0.030 | <0.030 | - | - | - |
C70U, U7A, C70W1, C70W2 - forskrift og forrit
Djúpt og yfirborðsherjandi kolefnisstál með lægsta kolefnisinnihald N12E kolefnisefna. Það sýnir mikla höggþol, högg og tiltölulega mikla hörku. Ef við tölum um galla þess einkennist það af lágu slitþoli og lítilli vélhæfni. N7E er notað til framleiðslu á tréverkfærum, mjúkum steinum, skurðarbrettum, litlum heitum gatamótum, smíðahamrum. Í sumum tilfellum er hægt að nota það í staðinn fyrir gormstál
Vélrænir eiginleikar U7A, C70W1, C70W2
Mjúkt ástand - hörku<187 HB Estado endurecido - dureza >57HRC
Hitameðferð: ferli og hitastig:
Mýkingarglæðing við 680 - 710 C Léttarglæðing við 600 - 700 C Temp herða við 780 - 820 C Temp slokknun við 170 - 190 C
Í þeim eiginleikum sem nefnd eru, útvegar fyrirtækið
Heitvalsaðar stangir C70U, C70W1, C70